Posteriorly, graphene-PEDOT:PSS films were fabricated considering xGnP-H5® or Celtig LCC® as graphene samples. The proportion used was 1:1 in weight of the graphene source and PEDOT:PSS; however, in the case of Celtig LCC®, to check the effect of the film thickness in G, it was also considered a higher loading of each element. Table 4 shows the obtained results. Visibly, the introduction of PEDOT:PSS (with a WF value near -5.1 eV and a G of 2.6×10-2 -1) led to enhanced electrical conducting graphene-based films. Nevertheless, as it was expected, higher loads result in better G but also in thicker films (hampering the CE transparency).