Common use of Car Wash Test Clause in Contracts

Car Wash Test. 4.8.1. Apparatus The apparatus shall comprise at least the following individual components: 4.8.1.1. Washing brush: Diameter (1,000 ± 40) mm Width Minimum 300 mm Rotation speed (127 ± 5) rev/min. brush rotationrotates in the opposite direction relative to the direction of travel of the test panel holder Material polyethylene Bristle profile x-shaped, spliced Bristle thickness (0.8 ± 0.2) mm Bristle length (440 ± 20) mm visible Penetration depth (100 ± 20) mm (see Figure 7) The state of the brushes shall be regularly controlled. At least one monitoring of the total amount of operating hours in use for the brush and an automatic replacement of the brush shall be conducted as soon as 30 operating hours are reached (30 hours equates around 300 test runs since one test takes around 6 minutes). The amount of operating hours shall be reported with the haze increase result of the sample.

Car Wash Test. 4.8.1. Apparatus The apparatus shall comprise at least the following individual components: 4.8.1.1. Washing brush: Diameter (1,000 ± 40) mm Width Minimum 300 mm Rotation speed (127 ± 5) rev/min. min brush rotationrotates in the opposite direction relative to the direction of travel of the test panel holder Material polyethylene Bristle profile x-shaped, spliced Bristle thickness (0.8 ± 0.2) mm Bristle length (440 ± 20) mm visible Penetration depth (100 ± 20) mm (see Figure 7) The state of the brushes shall be regularly controlled. At least one monitoring of the total amount of operating hours in use for the brush and an automatic replacement of the brush shall be conducted as soon as 30 operating hours are reached (30 hours equates around 300 test runs since one test takes around 6 minutes). The amount of operating hours shall be reported with the haze increase result of the sample.

Car Wash Test. 4.8.1. Apparatus The apparatus shall comprise at least the following individual components: 4.8.1.1. Washing brush: Diameter (1,000 ± 40) mm Width Minimum 300 mm Rotation speed (127 ± 5) rev/min. brush rotationrotates rotation rotates in the opposite direction relative to the direction of travel of the test panel holder Material polyethylene Bristle profile x-shaped, spliced Bristle thickness (0.8 ± 0.2) mm Bristle length (440 ± 20) mm visible 64 For Public Comment Only Penetration depth (100 ± 20) mm (see Figure 7) The state of the brushes shall be regularly controlled. At least one monitoring of the total amount of operating hours in use for the brush and an automatic replacement of the brush shall be conducted as soon as 30 operating hours are reached (30 hours equates around 300 test runs since one test takes around 6 minutes). The amount of operating hours shall be reported with the haze increase result of the sample.

Car Wash Test. 4.8.1. Apparatus The apparatus shall comprise at least the following individual components: 4.8.1.1. Washing brush: Diameter (1,000 ± 40) mm Width Minimum 300 mm Rotation speed (127 ± 5) rev/min. brush rotationrotates rotation rotates in the opposite direction relative to the direction of travel of the test panel holder Material polyethylene Bristle profile x-shaped, spliced Bristle thickness (0.8 ± 0.2) mm Bristle length (440 ± 20) mm visible Penetration depth (100 ± 20) mm (see Figure 7) The state of the brushes shall be regularly controlled. At least one monitoring of the total amount of operating hours in use for the brush and an automatic replacement of the brush shall be conducted as soon as 30 operating hours are reached (30 hours equates around 300 test runs since one test takes around 6 minutes). The amount of operating hours shall be reported with the haze increase result of the sample.

Car Wash Test. 4.8.1. Apparatus The apparatus shall comprise at least the following individual components: 4.8.1.1. Washing brush: Diameter (1,000 ± 40) mm Width Minimum 300 mm Rotation speed (127 ± 5) rev/min. min brush rotationrotates rotation rotates in the opposite direction relative to the direction of travel of the test panel holder Material polyethylene Bristle profile x-shaped, spliced Bristle thickness (0.8 ± 0.2) mm Bristle length (440 ± 20) mm visible Penetration depth (100 ± 20) mm (see Figure 7) The state of the brushes shall be regularly controlled. At least one monitoring of the total amount of operating hours in use for the brush and an automatic replacement of the brush shall be conducted as soon as 30 operating hours are reached (30 hours equates around 300 test runs since one test takes around 6 minutes). The amount of operating hours shall be reported with the haze increase result of the sample.