Curing of thermosetting resins. If a thermosetting resin is used, the resin shall be cured after filament winding. During the curing, the curing cycle (i.e. the time-temperature history) shall be documented. The curing temperature shall be controlled and shall not affect the material properties of the liner. The maximum curing temperature for cylinders with aluminium liners is 177 °C. 8.3.4. Auto-frettage Auto-frettage, if used, shall be carried out before the hydrostatic pressure test. The auto-frettage pressure shall be within the limits established in paragraph 8.2.3. above, and the manufacturer shall establish the method to verify the appropriate pressure.
Appears in 5 contracts
Samples: Agreement Concerning the Adoption of Harmonized Technical United Nations Regulations, Agreement Concerning the Adoption of Harmonized Technical United Nations Regulations, Agreement Concerning the Adoption of Harmonized Technical United Nations Regulations
Curing of thermosetting resins. If a thermosetting resin is used, the resin shall be cured after filament winding. During the curing, the curing cycle (i.e. the time-temperature history) shall be documented. The curing temperature shall be controlled and shall not affect the material properties of the liner. The maximum curing temperature for cylinders with aluminium liners is 177 °C.C.
8.3.4. Auto-frettage Auto-frettage, if used, shall be carried out before the hydrostatic pressure test. The auto-frettage pressure shall be within the limits established in paragraph 8.2.3. above, and the manufacturer shall establish the method to verify the appropriate pressure.
Appears in 2 contracts
Samples: Agreement Concerning the Adoption of Uniform Technical Prescriptions for Wheeled Vehicles, Agreement Concerning the Adoption of Uniform Technical Prescriptions for Wheeled Vehicles
Curing of thermosetting resins. If a thermosetting resin is used, the resin shall be cured after filament winding. During the curing, the curing cycle (i.e. the time-temperature history) shall be documented. The curing temperature shall be controlled and shall not affect the material properties of the liner. The maximum curing temperature for cylinders with aluminium aluminum liners is 177 °C.C.
8.3.4. Auto-frettage Auto-frettage, if used, shall be carried out before the hydrostatic pressure test. The auto-frettage pressure shall be within the limits established in paragraph 8.2.3. above, and the manufacturer shall establish the method to verify the appropriate pressure.
Appears in 1 contract
Samples: Agreement Concerning the Adoption of Uniform Technical Prescriptions for Wheeled Vehicles