Stress corrosion cracking test. For TPRDs containing components made of a copper-based alloy (e.g. brass), one TPRD unit is tested. All copper alloy components exposed to the atmosphere shall be degreased and then continuously exposed for ten days to a moist ammonia-air mixture maintained in a glass chamber having a glass cover. Aqueous ammonia having a specific gravity of 0.94 is maintained at the bottom of the glass chamber below the sample at a concentration of at least 20 ml per litre of chamber volume. The sample is positioned 35 (±5) mm above the aqueous ammonia solution and supported in an inert tray. The moist ammonia-air mixture is maintained at atmospheric pressure at 35 (±5) °C. Copper-based alloy components shall not exhibit cracking or delaminating due to this test.
Appears in 3 contracts
Samples: data.thaiauto.or.th, www.unece.org, undocs.org
Stress corrosion cracking test. For TPRDs containing components made of a copper-based alloy (e.g. brass), one TPRD unit is tested. All copper alloy components exposed to the atmosphere shall be degreased and then continuously exposed for ten days to a moist ammonia-air ammonia‑air mixture maintained in a glass chamber having a glass cover. Aqueous ammonia having a specific gravity of 0.94 is maintained at the bottom of the glass chamber below the sample at a concentration of at least 20 ml per litre of chamber volume. The sample is positioned 35 (±5) mm above the aqueous ammonia solution and supported in an inert tray. The moist ammonia-air mixture is maintained at atmospheric pressure at 35 (±5) °C. Copper-based alloy components shall not exhibit cracking or delaminating due to this test.
Appears in 2 contracts
Stress corrosion cracking test. For TPRDs containing components made of a copper-based alloy (e.g. brass), one TPRD unit is tested. All copper alloy components exposed to the atmosphere shall be degreased and then continuously exposed for ten 10 days to a moist ammonia-air mixture maintained in a glass chamber having a glass cover. Aqueous ammonia having a specific gravity of 0.94 is maintained at the bottom of the glass chamber below the sample at a concentration of at least 20 ml per litre of chamber volume. The sample is positioned 35 (±5) mm above the aqueous ammonia solution and supported in an inert tray. The moist ammonia-air mixture is maintained at atmospheric pressure at 35 (±5) °C. Copper-Copper- based alloy components shall not exhibit cracking or delaminating due to this test.
Appears in 1 contract
Samples: www.h2fc.eu
Stress corrosion cracking test. For TPRDs containing components made of a copper-based alloy (e.g. brass), one TPRD unit is tested. All copper alloy components exposed to the atmosphere shall be degreased and then continuously exposed for ten days to a moist ammonia-air mixture maintained in a glass chamber having a glass cover. Aqueous ammonia having a specific gravity of 0.94 is maintained at the bottom of the glass chamber below the sample at a concentration of at least 20 ml per litre of chamber volume. The sample is positioned 35 (±5) mm above the aqueous ammonia solution and supported in an inert tray. The moist ammonia-ammonia- air mixture is maintained at atmospheric pressure at 35 (±5) °C. Copper-based alloy components shall not exhibit cracking or delaminating due to this test.
Appears in 1 contract
Samples: data.thaiauto.or.th